Aortha EVA Foam Sheet | Density A65 - Very Firm - 1000 x 1000mm

Commonly used for shoe lifts, heel lifting, block heels, wedge bottoms, rigid orthoses and a variety of commercial uses.

As low as £8.76 Sheet size: 1000 x 800mm
Aortha
GB https://schema.org/MerchantReturnFiniteReturnWindow 14 https://schema.org/ReturnByMail https://schema.org/FreeReturn
GB
5.95 18 GBP
0 1 DAY
1 3 DAY

2 Day Tracked Delivery
PayPal | Apple Pay | Google Pay
Same Day Despatch - Before 2.30pm
Aftersales Support
Buy | Try | Review = 20% OFF Next Order
ISO 13485 Supplier for Medical Devices
Product Description

Aortha High Density EVA Features and Benefits:

Commonly used for shoe lifts, heel lifting, block heels, wedge bottoms, rigid orthoses and a variety of commercial uses.

Mouldable between 120°C and 170°C depending on density with an average oven time of 2 minutes per mm.

The ideal temperature for thermo-moulding Aortha EVA depends on the material thickness and hardness.
 
The standard principles would be:
1. Shore A25-A35 and 15mm EVA material: 100-130ºC temperature during 30 to 90 seconds exposure.
2. Shore A50 and 15mm EVA material: 110-140ºC temperature during 30 to 120 seconds exposure.
3. Shore A65 and 15mm EVA material: 120-150ºC temperature during 30 to 140 seconds exposure.
 
It is important to indicate the aforementioned conditions should be adjusted according to the following patterns:
•The thinner the material the lower the temperature or the exposure timing. The only effective way to determine heating times based on variable thickness and sheet size, is to test in stages based on the above guidelines.
 
• The heat source is also important; a direct infrared radiation will be much more aggressive than heating a piece with a circulating air system, meaning the temperature should be adjusted accordingly. Again, test in stages as per above.
 
• In general, EVA copolymers should not be extruded hotter than 200°C since degradation may occur.
 
• Degradation products include the elimination of acetic acid, which can account for a “vinegar” odour and corrosion of some materials.